Synthesis and characterization of magnetic Fe 3 O 4 @CaSiO 3 composites and evaluation of their adsorption characteristics for heavy metal ions

Abstract

A two-component material (Fe₃O₄@CaSiO₃) with an Fe₃O₄ magnetite core and layered porous CaSiO₃ shell from calcium nitrate and sodium silicate was synthesized by precipitation. The structure, morphology, magnetic properties, and composition of the Fe₃O₄@CaSiO₃ composite were characterized in detail, and its adsorption performance, adsorption kinetics, and recyclability for Cu²⁺, Ni²⁺, and Cr³⁺ adsorption were studied. The Fe₃O₄@CaSiO₃ composite has a 2D core–layer architecture with a cotton-like morphology, specific surface area of 41.56 m²/g, pore size of 16 nm, and pore volume of 0.25 cm³/g. The measured magnetization saturation values of the magnetic composite were 57.1 emu/g. Data of the adsorption of Cu²⁺, Ni²⁺, and Cr³⁺ by Fe₃O₄@CaSiO₃ fitted the Redlich–Peterson and pseudo-second-order models well, and all adsorption processes reached equilibrium within 150 min. The maximum adsorption capacities of Fe₃O₄@CaSiO₃ toward Cu²⁺, Ni²⁺, and Cr³⁺ were 427.10, 391.59, and 371.39 mg/g at an initial concentration of 225 mg/L and a temperature of 293 K according to the fitted curve with the Redlich–Peterson model, respectively. All adsorption were spontaneous endothermic processes featuring an entropy increase, including physisorption, chemisorption, and ion exchange; among these process, chemisorption was the primary mechanism. Fe₃O₄@CaSiO₃ exhibited excellent adsorption, regeneration, and magnetic separation performance, thereby demonstrating its potential applicability to removing heavy metal ions.

from Energy Ecology Environment Ambio via Terpsi Hori on Inoreader http://bit.ly/2MJDUzO