Physical and chemical properties of model composites containing quaternary ammonium methacrylates

Publication date: Available online 10 November 2017
Source:Dental Materials
Author(s): Marina Lermenn Vidal, Guilherme Ferreira Rego, Gil Mendes Viana, Lucio Mendes Cabral, Juliana Primo Basílio Souza, Nick Silikas, Luis Felipe Schneider, Larissa Maria Cavalcante
ObjectiveInvestigate physical and chemical properties of model composites formulated with quaternary ammonium salt monomers (QAS) at different concentrations and alkyl chains lengthsMethodsQAS with 12 dimethylaminododecyl methacrylate (DMADDM) and 16 dimethylaminohexadecyl methacrylate (DMAHDM) chains lengths were synthesized and incorporated at 5 and 10% in model composites, resulting in four groups: G12.5 (DMADDM 5%), G12.10 (DMADDM 10%), G16.5 (DMAHDM 5%), G16.10 (DMAHDM 10%). One group was used as control group (CG 0%). Degree of conversion (DC); water sorption (WS) and solubility (SL); hygroscopic expansion (HE); degradation temperature (DT); glass transition temperature (Tg) and polymerization shrinkage (PS) were determined. Knoop hardness (KNH), flexural strength (FS) and elastic modulus (EM) were measured before and after storage Data were submitted to ANOVA and Tukey's test (p≤0.05).ResultsDC ranged between 76.1 (G12.10) and 70.7 (G16.5) %; CG had the lowest WS, SL and HE. There was no statistical difference for PS and FS. KHN values ranged between 30.2 (GC) and 25 (G16.10) and after storage the performance was depended on QAS concentration and chain length. For EM, CG had the highest values before and after storage and no difference was observed in the QAS groups before storage. After storage, the results were dependent on QAS concentration (3.5-4.3GPa).SignificanceIn general, the addition of QAS increased composite's degradation compared with the CG. In the tested QAS, the addition of DMADDM at 5% concentration resulted in a less degradable material.



from ! ORL Sfakianakis via paythelady.61 on Inoreader http://ift.tt/2zuoOtV
via IFTTT