Ultralow thermal conductivity of cerium-doped Nd 2 Zr 2 O 7 over a wide doping range

Abstract

In this paper, we report an ultralow thermal conductivity and a high-temperature phase stability of the (Nd_1−x Ce_x )₂Zr₂O_7+x system over the temperature range from room temperature to 1600 °C and over a wide composition range (0.2 ≤ x ≤ 0.8), and the (Nd_1−x Ce_x )₂Zr₂O_7+x system is therefore considered a strong candidate material for the fabrication of next-generation high-temperature thermal barrier coatings. The observed thermal conductivities (0.65–1.0 W/mK) are about 60–40% lower than those of undoped Nd₂Zr₂O₇ over the same temperature range (100–700 °C) and indicate a glass-like behavior. For comparison, the variation in the thermal conductivity with the temperature of the (Gd_1−x Ce_x )₂Zr₂O_7+x system with similar point defects was also measured, and the observed behavior was almost the same as that of undoped Gd₂Zr₂O₇ and was mostly determined by phonon–phonon scattering (λ ∝ 1/T). The effect of point defect scattering and strong phonon scattering sources (rattlers) on the thermal conductivity is also discussed in this paper. The results of this study suggest that the ultralow thermal conductivity of (Nd_1−x Ce_x )₂Zr₂O_7+x can be attributed to the presence of rattlers because of the large difference between the ionic radii of the Nd³⁺ and Ce⁴⁺ ions.

from ! Medicine by Alexandros G. Sfakianakis via als.fakia on Inoreader http://ift.tt/2smIImM
via IFTTT